DATE | HS_CODE | Product Description | Trademark | Country | Net Weight | Statistical Cost | Place | Shipper Name | Consignee Name |
---|
2017-11-03 | 7601208002 | Untreated ALUMINUM ALLOY SECONDARY bullion (chushka) COMPOSITION: AL-88.528-92.859%, MG-0.330-0.450%, PB-0.000-0.060%, CU-1.040-2.250% Tensile strength 83-120MPA at 25 degrees C. , CM. Supplement is designed to produce a wide CI | ABSENT | JAPAN | 54565 | 96580,05 | ST PETERSBURG | ***** | ***** |
2017-11-09 | 7601208002 | Untreated ALUMINUM ALLOY SECONDARY bullion (chushka) COMPOSITION: AL-88.487-93.405%, MG-0.360-0.450%, PB-0.000-0.040%, CU-1.010-1.820% Tensile strength 83-120MPA at 25 degrees C. , CM. Supplement is designed to produce a wide CI | ABSENT | JAPAN | 54376 | 97333,04 | ST PETERSBURG | ***** | ***** |
2017-11-13 | 7601208002 | Untreated ALUMINUM ALLOY SECONDARY bullion (chushka) COMPOSITION: AL-88.470-92.849%, MG-0.300-0.450%, PB-0.000-0.100%, CU-1.040-2.050% Tensile strength 83-120MPA at 25 degrees C. , CM. Supplement is designed to produce a wide CI | ABSENT | JAPAN | 54573 | 97685,67 | ST PETERSBURG | ***** | ***** |
2017-11-14 | 2845909000 | Stable isotopes for medical and laboratory purposes. Not for military purposes. Not a hazardous waste. Packed in cardboard boxes. CM. Calcium supplement, enriched in the CA-43 to 62.20%. WEIGHT 30.0 mg. PROVIDED IN THE FORM CARB | *** | JAPAN | 0.131 | 4089,9 | TOKYO | ***** | ***** |
2017-11-17 | 7601208002 | Untreated ALUMINUM ALLOY SECONDARY bullion (chushka) COMPOSITION: AL-88.385-92.084%, MG-0.320-0.450%, PB-0.000-0.090%, CU-1.030-2.050% Tensile strength 83-120MPA at 25 degrees C. , CM. Supplement is designed to produce a wide CI | ABSENT | JAPAN | 54990 | 99256,95 | ST PETERSBURG | ***** | ***** |
2017-11-20 | 7601208002 | Untreated ALUMINUM ALLOY SECONDARY bullion (chushka) COMPOSITION: AL-88.377-92.580%, MG-0.320-0.450%, PB-0.000-0.090%, CU-1.090-2.030% Tensile strength 83-120MPA at 25 degrees C. , CM. Supplement is designed to produce a wide CI | ABSENT | JAPAN | 54472 | 98321,96 | ST PETERSBURG | ***** | ***** |
2017-11-23 | 7601208002 | Untreated ALUMINUM ALLOY SECONDARY bullion (chushka) COMPOSITION: AL-89.158-92.617%, MG-0.330-0.480%, PB-0.020-0.090%, CU-1.020-2.440% Tensile strength 83-120MPA at 25 degrees C. , CM. Supplement is designed to produce a wide CI | ABSENT | JAPAN | 54536 | 98437,48 | ST PETERSBURG | ***** | ***** |
2017-11-29 | 2917330000 | INDUSTRIAL based modifier plasticizer (diisononyl phthalate). Are plasticizers diisononyl phthalate as a viscous PASTE black with a faint characteristic odor supplemented with 10% TUBALL SWNTs | OCSIAL TUBALL | JAPAN | 2 | 310 | NOVOSIBIRSK | ***** | ***** |
2017-11-29 | 7601208002 | Untreated ALUMINUM ALLOY SECONDARY bullion (chushka) COMPOSITION: AL-88.478-92.310%, MG-0.330-0.450%, PB-0.000-0.095%, CU-1.090-2.290% Tensile strength 83-120MPA at 25 degrees C. , CM. Supplement is designed to produce a wide CI | ABSENT | JAPAN | 54937 | 99161,29 | ST PETERSBURG | ***** | ***** |