DATE | HS_CODE | Product Description | Trademark | Country | Net Weight | Statistical Cost | Place | Shipper Name | Consignee Name |
---|
2017-09-05 | 3816000000 | Refractory material for lining of furnaces: Ramming WET WEIGHT CONTAINING CARBON BASED ON bauxite and silica carbide, The maximum recommended temperature 1600 C. COMPOSITION: ALUMINUM DIOXIDE (AL2O3) - 61%, silicon carbide (SIC) - 14,5%, carbon ( C | *** | GERMANY | 54000 | 61465,85 | *** | ***** | ***** |
2017-09-14 | 3816000000 | Refractory STRUCTURE (CONCRETE) for lining the gutter blast furnace. It provided as a powdered Printed MIXTURE NAOSNOVE bauxite, silicon carbide and carbon. APPLY FOR steelworks MARK SEVEN RAM 2565 KX; TOTAL: 22000KG. : SEVEN | *** | SLOVENIA | 22000 | 32462,58 | *** | ***** | ***** |
2017-09-21 | 3816000000 | CM. ANNEX Refractory mixture based on bauxite DIDURIT B83-6. Refractory concrete. COMPOSITION: SIO2-13,47%, FE2O3-1,16%, AL2O3- 80,68%, CAO-1,22%, TIO2-2,63%, CR2O3-0.04%, P2O5-0.20%, MGO-0.09 %, K2O-0.25%, NA2O-0.11, ZRO2-0.15. MIXTURE LEGRIT 135-1,3 0-4. Went | *** | GERMANY | 52370 | 73767,24 | *** | ***** | ***** |
2017-09-25 | 3816000000 | ROOM PART furnace pyrolysis plant: OGNEUPORNOY cement grade CA-50: DRY MIXTURE ALUMINOUS consisting of refractory cement, lime CONTAINING CORUND (AL2O3), silicon carbide and bauxite CLINKER. Refractory: 1580GRADUSOV Celsius. | *** | CHINA | 150 | 120,87 | *** | ***** | ***** |
2017-11-08 | 3816000000 | Refractory concrete for the arch of Particleboard, Mark PN-TSF3-E, NOT FOR FOUNDRY: Functionality - FOR ARCH arc furnace; BASIC MATERIALS - bauxite, corundum; Bundles - bitumen; METHOD OF MANUFACTURING - crushing, blending, mixed | PN | CHINA | 3000 | 3120,88 | Novotroitskaya | ***** | ***** |
2017-11-09 | 3816000000 | Refractory CONSTRUCTION OF CEMENT BASED COMPOSITION USED IN CONSTRUCTION OF PETROCHEMICAL, powdered, PORTLAND CEMENT BASED ON (50%), with the addition of bauxite (25-50%) pulp (1-10%), quartz (less than 1%), clays ( 1-10%) and | MONOKOTE | KOREA REPUBLIC OF | 40320 | 40512 | Alexina | ***** | ***** |
2017-11-12 | 3816000000 | REFRACTORY MIXTURE BASED bauxites containing alumina (AL2O3- 57,0%), silicon carbide (SIC -34,0%), silicon oxide (SIO2 -3,0%), Carbon (C -2,0%), OXIDE CALCIUM (CAO- 0,6%) INTENDED FOR STACKING METHOD OF VIBRATION (in big bags 1000 kg | "CALDERYS" | GERMANY | 22000 | 28299,73 | NEUWIED | ***** | ***** |
2017-11-13 | 3816000000 | Refractory castable (TORKET WEIGHT) ON THE BASIS bauxites containing alumina (AL2O3- 62,5%), silicon carbide (SIC -19,2%), silicon oxide (SIO2 -7,8%), Carbon (C -4, 8%), calcium oxide (CAO- 2,4%), STYLING BY guniting, in big- | "CALDERYS" | FRANCE | 70000 | 74735,43 | SEZANNE | ***** | ***** |
2017-11-30 | 3816000000 | Refractory castable (TORKET WEIGHT) ON THE BASIS bauxites containing alumina (AL2O3-62,5%), silicon carbide (SIC-19,2%), silicon oxide (SIO2 -7,8%), Carbon (C-4, 8%), calcium oxide (CAO-2,4%), STYLING BY guniting, in big-bags P | "CALDERYS" | GERMANY | 75000 | 76567,27 | NEUWIED | ***** | ***** |
2017-11-30 | 3816000000 | REFRACTORY MIXTURE BASED bauxites containing alumina (AL2O3-57,0%), silicon carbide (SIC-34,0%), silicon oxide (SIO2-3,0%), Carbon (C -2,0%), OXIDE CALCIUM (CAO-0,6%) INTENDED FOR STACKING METHOD OF VIBRATION, in big-bags 1000 kg | "CALDERYS" | GERMANY | 5000 | 6545,96 | NEUWIED | ***** | ***** |